Analysis of Fe and Co binary catalysts in chemical vapor deposition growth of single-walled carbon nanotubes

Abstract

Metal catalysts play a pivotal role in the growth of single-walled carbon nanotubes (SWCNTs), with binary metallic catalysts emerging as an efficient SWCNT synthesis strategy. Among these, iron (Fe), cobalt (Co), and their alloys are particularly effective. However, prior studies have predominantly employed Fe--Co alloy catalysts with fixed atomic ratios as well as unchanged chemical vapor deposition (CVD) conditions, leaving the influence of variable Fe--Co compositions and CVD growth parameters on SWCNT synthesis poorly understood. This study focuses on the role of Fe--Co catalyst ratios, with the aim of elucidating the distinct contributions of Fe and Co atoms in the growth of SWCNTs. By systematically exploring a wide range of Fe--Co ratios and growth conditions, we identified Fe$_{0.75}$Co$_{0.25}$ as a highly efficient binary catalyst at 850~$^\circ$C, primarily forming catalyst clusters with diameters of 2.5--6~nm and yielding SWCNTs with diameters ranging from 0.9--1.1~nm. On the other hand, Fe$_{0}$Co$_{1}$ exhibited higher catalytic activity at 600~$^\circ$C, generating smaller catalyst clusters of 1.5--5~nm and producing SWCNTs with reduced diameters of about 0.6--0.9~nm. Transmission electron microscope (TEM) and energy dispersive X-ray spectroscopy (EDS) analyses reveal that high SWCNT yields correlate with the formation of uniformly sized Fe--Co catalyst particles with surface-segregated Co that optimizes carbon solubility. Molecular dynamics (MD) simulations further corroborate these findings, demonstrating that the structure and melting behavior of Fe$_x$Co$_{1-x}$ clusters depend on cluster size and composition.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Qingmei Hu, Ya Feng, Wanyu Dai, Daisuke Asa, Daniel Hedman, Aina Fito Parera, Yixi Yao, Yongjia Zheng, Kaoru Hisama, Gunjan Auti, Hirofumi Daiguji, Christophe Bichara, Shohei Chiashi, Yan Li, Wim Wenseleers, Dmitry Levshov, Sofie Cambre, Keigo Otsuka, Rong Xiang, Shigeo Maruyama. 2025-07-23. Analysis of Fe and Co binary catalysts in chemical vapor deposition growth of single-walled carbon nanotubes. https://arxiv.org/abs/2507.17891

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Uncertainty quantification design principles for machine learning interatomic potentials: lessons learned from hierarchical Bayesian inference

Reliable uncertainty quantification (UQ) remains a major challenge for machine learning interatomic potentials (MLIPs). Here, we benchmark UQ strategies for message passing neural networks such as MACE and Gaussian process (GP)-based interatomic potentials using coupled-cluster reference data for argon as a test case. We develop a hierarchical GP potential combining physics-informed priors with Bayesian propagation of hyperparameter uncertainty that retains useful discrimination of prediction errors while remaining conservative rather than overconfident, with a probabilistic structure that allows the sources of predictive uncertainty to be explicitly dissected. These results expose important distinctions between accuracy, calibration, sharpness, and error discrimination and provide practical design principles for MLIP UQ in uncertainty-critical applications.

cond-mat.mtrl-sci

Structural Phase Separation Couples to Charge-Density-Wave Formation in Kagome Metal FeGe

The intertwining of charge, spin, and lattice degrees of freedom underlies the emergent properties of correlated materials. A recent prominent example is the kagome metal FeGe, which hosts coexisting charge density wave (CDW) and antiferromagnetic orders, accompanied by a lattice distortion associated with partial Ge-Ge dimerization. Using temperature-dependent high-resolution X-ray diffraction measurements, we observed a robust splitting of the lattice reflection into two coexisting peaks with distinct lattice constants at the CDW transition temperature TCDW, providing direct evidence for a first-order structural phase transition that is absent in samples with suppressed CDW order. Furthermore, the long-range CDW order was found to be only commensurate with lattice structures with the compressed out-of-plane lattice constant. The Landau free energy analysis shows that strong lattice-charge coupling is a key factor in stabilizing long-range CDW order. Our work clarifies the critical role of structural transformation in the CDW formation and opens opportunities for strain control of electronic phases in FeGe.

cond-mat.mtrl-sci

Bottlenecks in Hamiltonian-Adaptive Resolution Simulation Method for Modeling Interfaces

The Hamiltonian-Adaptive Resolution Simulation (H-AdResS) method allows to combine atomistic and particle-based coarse-grained models in a single simulation box, which makes it very attractive to model systems containing interfaces or reactive regions surrounded by an interacting environment. In our previous work [J. Chem. Inf. Model. (2026) 66 (15): 9215-9225], we implemented H-AdResS in LAMMPS (2 Aug 2023 version) and extended its use to interfaces, focusing on MOF/CO$_2$ interfaces as an example. We found that, despite its advantages, using this method properly for this kind of systems is not trivial. In this work, an in-depth analysis of the impact of the choice of thermostatting schemes and long-range electrostatics models is presented. Even though its Hamiltonian formulation enables performing H-AdResS simulations within constant temperatures ensembles, not every thermostat is appropriate. We demonstrate that Langevin thermostat is a reliable choice for this method, while Nosé-Hoover results in artifacts. In addition, we show that using short-range models such as the Damped Shifted Force method for electrostatics, a popular choice for H-AdResS simulations, can lead to non-physical results when modeling interfaces. The need of capping strategies to deal with discontinuities in forces and energies arising from abrupt changes in resolution is also discussed. Finally, the impossibility of changing the definition of the H-AdResS Hamiltonian to include a gradual interpolation of the bonded degrees of freedom is discussed. We hope that this contribution helps the reader to appropriately set up H-AdResS simulations and to assess if this method can be used to accurately model their system of interest.

cond-mat.mtrl-sci