Hall-effect in LuNi_2B_2C and YNi_2B_2C borocarbides: a comparative study

Abstract

The Hall effect in LuNi_2B_2C and YNi_2B_2C borocarbides has been investigated in normal and superconducting mixed states. The Hall resistivity rho_{xy} for both compounds is negative in the normal as well as in the mixed state and has no sign reversal below T_c typical for high-T_c superconductors. In the mixed state the behavior of both systems is quite similar. The scaling relation rho_{xy}\simρ_{xx}^β(ρ_{xx} is the longitudinal resistivity) was found with β=2.0 and 2.1 for annealed Lu- and Y-based compounds, respectively. The scaling exponent βdecreases with increasing degree of disorder and can be varied by annealing. This is attributed to a variation of the strength of flux pinning. In the normal state weakly temperature dependent Hall coefficients were observed for both compounds. A distinct nonlinearity in the ρ_{xy} dependence on field H was found for LuNi_2B_2C in the normal state below 40K, accompanied by a large magnetoresistance (MR) reaching +90% for H=160kOe at T=20K. At the same time for YNi_2B_2C only linear ρ_{xy}(H) dependences were observed in the normal state with an approximately three times lower MR value. This difference in the normal state behavior of the very similar Lu- and Y-based borocarbides seems to be connected with the difference in the topology of the Fermi surface of these compounds.