arXiv subjects

Triloki

Publications and source records attributed to Triloki.

16 recordsLinked to original sources

arXiv2025

Nanodiamond photocathodes for MPGD-based single photon detectors

This study investigates the suitability of Hydrogenated NanoDiamond (HND) materials as an alternative for CsI in MPGD-based photon detectors. The research focuses on characterizing HND photocathodes coupled with THGEM + Micromegas-based detectors. The HND grains were prepared via hydrogenation and stored in water for more than two years. They were then coated on PCB discs or THGEMs using a pulsed spray technique. The resulting quantum efficiency (QE) values (~4% at 122 nm) were found to be within a factor of 10 of the best freshly hydrogenated samples reported in the literature ( ~40% at 120 nm). The robustness of reflective HND photocathodes against ion bombardment was measured to be about 10 times larger than the corresponding CsI one after the same charge accumulation. Furthermore, THGEM characterization indicates minimal alteration in response after HND coatings. These results suggest that HND holds potential as a more robust photocathode for gaseous detectors, offering improved performance in single-photon detection applications.

physics.ins-det↗

arXiv2024

Study of nanodiamond photocathodes for MPGD-based detectors of single photons

The proposed new Electron-Ion Collider poses a technical and intellectual challenge for the detector design to accommodate the long-term diverse physics goals envisaged by the program. This requires a 4{\pi} detector system capable of reconstructing the energy and momentum of final state particles with high precision. The Electron-Ion Collider also requires identification of particles of different masses over a wide momentum range. A diverse spectrum of Particle Identification detectors has been proposed. Of the four types of detectors for hadron identification, three are based on Ring Imaging Cherenkov Counter technologies, and one is realized by the Time of Flight method. The quest for a novel photocathode, sensitive in the far vacuum ultra violet wavelength range and more robust than cesium iodide, motivated an R&D programme to explore nano-diamond (ND) based photocathodes, started by a collaboration between INFN and CNR Bari and INFN Trieste. Systematic measurements of the photo emission in different Ar-CH4 and Ar-CO2 gas mixtures with various types of ND powders and Hydrogenated ND (H-ND) powders are reported. A first study of the response of THGEMs coated with different photocathode materials is presented. The progress of this R&D programme and the results obtained so far by these exploratory studies are described.

physics.ins-det↗

arXiv2024

Progress in coupling MPGD-based Photon Detectors with Nanodiamond Photocathodes

The next generation of gaseous photon detectors is requested to overcome the limitations of the available technology, in terms of resolution and robustness. The quest for a novel photocathode, sensitive in the far vacuum ultra violet wavelength range and more robust than present ones, motivated an R&D programme to explore nanodiamond based photoconverters, which represent the most promising alternative to cesium iodine. A procedure for producing the novel photocathodes has been defined and applied on THGEMs samples. Systematic measurements of the photo emission in different Ar/CH4 and Ar/CO2 gas mixtures with various types of nanodiamond powders have been performed. A comparative study of the response of THGEMs before and after coating demonstrated their full compatibility with the novel photocathodes.

physics.ins-det↗

arXiv2023

Long term experience with perfluorobutane in COMPASS RICH

COMPASS RICH-1 has used high-purity perfluorobutane as radiator gas since 2001. The operation and control of the radiator gas has evolved over years with continuous improvements. We report on the experience gained in the 20 year-long operation of perfluorobutane as COMPASS RICH radiator. Very accurate values for the radiator gas refractive index are needed for high-performance particle identification. The procedure has evolved over years and the one presently in use, which provides refractive index estimate at the 1 ppm level, is discussed. Perfluorobutane procurement is becoming challenging, and the minimization of material waste is now a priority for the protection of the environment. Commercially available perfluorobutane needs dedicated filtering before usage and typical material losses in the filtering procedure were around 30%. Recent efforts allowed us to reduce them to about 5%. A potential alternative to fluorocarbon radiators in gaseous RICHes is also presented.

physics.ins-det↗

arXiv2020

Nanodiamond photocathodes for MPGD-based single photon detectors at future EIC

We are developing gaseous photon detectors for Cherenkov imaging applications in the experiments at the future Electron Ion Collider. CsI, converting photons in the far ultraviolet range, is, so far, the only photoconverter compatible with the operation of gaseous detectors. It is very delicate to handle due to its hygroscopic nature: the absorbed water vapour decomposes the CsI molecule. In addition, its quantum efficiency degrades under ion bombardment. These are the key reasons to quest for novel, less delicate materials for photocathodes adequate for gaseous photon detectors. Layers of hydrogenated nanodiamond particles have recently been proposed as an alternative material and have shown promising characteristics. The performance of nanodiamond photocathodes coupled to thick GEM-based detectors is the object of our ongoing R\&D. The first phase of these studies includes the characterization of thick GEM coated with nanodiamond layers and the robustness of its photoconverting properties with respect to the bombardment by ions from the multiplication process in the gaseous detector. The approach is described in detail as well as all the results obtained so far within these exploratory studies.

physics.ins-det↗

arXiv2019

Nanodiamond photocathodes for MPGD-based single photon detectors at future EIC

The design of a Ring Imaging CHerenkov (RICH) detector for the identification of high momentum particles at the future Electron Ion Collider (EIC) is extremely challenging by using current technology. Compact collider setups impose to construct RICH with short radiator length, hence limiting the number of generated photons. The number of detected photons can be increased by selecting the far UV region. As standard fused-silica windows is opaque below 165 nm, a windowless RICH can be a possible approach. CsI is widely used photocathode (PC) for photon detection in the far UV range. Due to its hygroscopic nature it is very delicate to handle. In addition, its Quantum Efficiency (QE) degrades in high intensity ion fluxes. These are the key reasons to quest for novel PC with sensitivity in the far UV region. Recent development of layers of hydrogenated nanodiamond powders as an alternative PC material and their performance, when coupled to the THick Gaseous Electron Multipliers (THGEM)-based detectors, are the objects of an ongoing R\&D. We report here some preliminary results on the initial phase of these studies.

physics.ins-det↗

arXiv2019

The high voltage system with pressure and temperature corrections for the novel MPGD-based photon detectors of COMPASS RICH-1

The novel MPGD-based photon detectors of COMPASS RICH-1 consist of large-size hybrid MPGDs with multi-layer architecture including two layers of Thick-GEMs and a bulk resistive MicroMegas. The top surface of the first THGEM is coated with a CsI film which also acts as photo-cathode. These detectors have been successfully in operation at COMPASS since 2016. Concerning bias-voltage supply, the Thick-GEMs are segmented in order to reduce the energy released in case of occasional discharges, while the MicroMegas anode is segmented into pads individually biased with positive voltage while the micromesh is grounded. In total, there are about ten different electrode types and more than 20000 electrodes supplied by more than 100 HV channels, where appropriate correlations among the applied voltages are required for the correct operation of the detectors. Therefore, a robust control system is mandatory, implemented by a custom designed software package, while commercial power supply units are used. This sophisticated control system allows to protect the detectors against errors by the operator, to monitor and log voltages and currents at 1 Hz rate, and automatically react to detector misbehaviour. In addition, a voltage compensation system has been developed to automatically adjust the biasing voltage according to environmental pressure and temperature variations, to achieve constant gain over time. This development answers to a more general need. In fact, voltage compensation is always a requirement for the stability of gaseous detectors and its need is enhanced in multi-layer ones. In this paper, the HV system and its performance are described in details, as well as the stability of the novel MPGD-based photon detectors during the physics data taking at COMPASS.

physics.ins-det↗

arXiv2018

Humidity effects on evolution of CsI thin Films: Fractal studies of rough surfaces

The present work investigates the morphological, micro-structural, compositional and fractal analysis for CsI thin films in case of "as-deposited" and "1 hour humid air aged". The variation of grain sizes obtained from transmission electron microscopy (TEM) technique are found to be in the range of ~ 313 nm to ~ 1058 nm. The average grain size is found to increase after exposing to humidity. The experimental values of interplanner spacing are found to be less than the standard value which signifies that a compressive stress is acting in the film. The elemental compositions of CsI film has been investigated by the means of energy dispersive X-ray spectroscopy (EDAX) technique. The atomic percentage of Cs:I (1:1) is found to be increased by a factor of two after exposing to humidity. The surface morphology of CsI thin films is analyzed by the atomic force microscopy (AFM) for both cases. The fractal analysis is performed on the AFM micrographs. The autocorrelation function and height-height correlation function is used to study the correlation properties of surface and roughness exponent. It is found that the fractal dimension is affected after exposing to humidity.

physics.ins-det↗

arXiv2018

Structural and optical properties of CsI thin films: Influence of film thickness and humidity

Structural and optical studies have been performed on the thermally-evaporated "as-deposited" and "humid air aged" CsI thin films. The structural analysis for both "as-deposited" and "humid air aged" films shows a well-oriented peaks position of (110) and (220) lattice planes with a compressive stress in the films. The crystal quality has been investigated through the structural parameters. The increase in peak intensity as well as sharpness with film thickness implies the improvement of crystallinity. The optical absorbance of CsI films has been analyzed in the wavelength range of 190 nm - 900 nm in order to estimate the band gap energy of the films. Slater's model has also been used to explain the degradation of band gap energy with the increase in crystallite size.

physics.ins-det↗

arXiv2018

Growth evolution of self-affine thermally evaporated KBr thin films: A fractal assessment

In this article, fractal concepts were used to explore the thermally evaporated potassium bromide thin films of different thicknesses 200, 300, and 500 nm respectively; grown on aluminium substrates at room temperature. The self-affine or self similar nature of growing surfaces was investigated by autocorrelation function and obtained results are compared with the morphological envelope method. Theoretical estimations revealed that the global surface parameters such as, interface width and lateral correlation length are monotonically decreased with increasing film thickness. Also, from height profile and A-F plots, it has been perceived that irregularity/ complexity of growing layers was significantly influenced by thickness. On the other hand, the fractal dimension and local roughness exponent, estimated by height-height correlation function, do not suggest such dependency.

cond-mat.mtrl-sci↗

arXiv2017

X-ray diffraction line profile analysis of KBr thin films

In the present work, the microcrystalline characteristics of KBr thin films have been investigated by evaluating the breadth of diffraction peak. The Williamson-Hall, the Size-Strain Plot and the single line Voigt methods are employed to deconvolute the finite crystallite size and microstrain contribution from the broaden X-ray profile. The texture coefficient and dislocation density have been determined along each diffraction peak. Other relevant physical parameters such as stress, Young's modulus and energy density are also estimated using Uniform Stress-Deformation and Uniform Deformation Energy Density approximation of Williamson-Hall method.

cond-mat.mtrl-sci↗

arXiv2017

Correlation between photoemissive and morphological properties of KBr thin film photocathodes

In the present work, the morphological properties of KBr photocathodes are correlated with their photoemissive behaviour using a combination of analyzing techniques including SEM, TEM and AFM. From morphological studies, it is observed that KBr films have granular characteristics with varied average grain size and grain density. Structure and orientation of individual grains have been investigated by selected area electron diffraction technique and found to be the crystalline in nature with a face centered cubic structure. It is evident from the AFM analysis that the root mean square roughness and maximum area peak height have been decreased with the deposition of more KBr layers. The photoemission studies reveal that the resultant photocurrent is enhanced with increasing film thickness and it is directly related to the surface area coverage and grain density.

physics.ins-det↗

arXiv2014

Optical and structural properties of CsI thin film photocathode

In the present work performance of cesium iodide thin film photocathode is studied in detail. The optical absorbance of cesium iodide thin films have been analyzed in the spectral range of 190 nm to 900 nm. The optical band gap energy of 500 nm thick cesium iodide film is calculated using Tauc plot from absorbance data. Refractive index is estimated from envelope plot of transmittance data using Swanepoel's method. Absolute quantum efficiency measurement has been carried out in the wavelength range of 150 nm to 200 nm. Crystallographic nature and surface morphology are investigated by X-ray diffraction, transmission electron microscopy and atomic force microscopy techniques. In addition, elemental composition result gained by energy dispersive X-ray analysis is also reported in the present work.

cond-mat.mtrl-sci↗

arXiv2014

Effect of humid air exposure on photoemissive and structural properties of KBr thin film photocathode

We have investigated the influence of water molecule absorption on photoemissive and structural properties of potassium bromide (KBr) thin film photocathode under humid air exposure at relative humidity (RH) 65%. It is evident from photoemission measurement that the photoelectron yield of KBr photocathode is degraded exponentially with humid air exposed time. Structural studies of the "as-deposited" and "humid air aged" films reveal that there is no effect of RH on film's crystalline face centered cubic (fcc) structure. However, the average crystallite size of "humid air exposed film" KBr film has been increased as compared to "as-deposited". In addition, topographical properties of KBr film are also examined by means of scanning electron microscope (SEM), transmission electron microscope (TEM) and atomic force microscope (AFM) and it is observed that granular characteristic of film has been altered, even for short exposure to humid air.

physics.ins-det↗

arXiv2014

Photoemission and optical constant measurements of Cesium Iodide thin film photocathode

The performance of cesium iodide as a reflective photocathode is presented. The absolute quantum efficiency of a 500 nm thick film of cesium iodide has been measured in the wavelength range 150 nm to 200 nm. The optical absorbance has been analyzed in the wavelength range 190 nm to 900 nm and the optical band gap energy has been calculated. The dispersion properties were determined from the refractive index using an envelope plot of the transmittance data. The morphological and elemental film composition have been investigated by atomic force microscopy and X-ray photo-electron spectroscopy techniques.

physics.ins-det↗

arXiv2012

Structural characterization of as-deposited cesium iodide films studied by X-ray diffraction and transmission electron microscopy techniques

In the present work, cesium iodide (CsI) thin films of different thickness have been prepared by thermal evaporation technique. The crystallite size and grain size of these films are compared by using X-ray diffraction (XRD) profile analysis as well as by transmission electron microscopy (TEM) counting, respectively. These two methods provide less deviation between crystallite size and grain size in the case of thin CsI films of 4 nm, but there is comparatively large difference in case of thicker CsI films (20 nm, 100 nm and 500 nm). It indicates that dislocations are arranged in a configuration which causes small orientational difference between two adjacent coherent regions. The size obtained from XRD corresponds to two separate regions, whereas in the TEM micrograph the two regions may seem to correspond one region particularly in case of thicker films. Other physical parameters such as strain, stress and deformation energy density are also estimated precisely for the prominent XRD peaks of thicker CsI films in the range $2\theta = 20^{0}-80^{0}$ by using a modified Williamson-Hall (W-H) analysis assuming uniform deformation model (UDM), uniform deformation stress model (UDSM) and uniform deformation energy density model (UDEDM).

cond-mat.mtrl-sci↗