arXiv2026

Weak Ferromagnetism in NiS$_2$ under Nanocrystallization

Structurally well-ordered NiS$_2$ nanocrystals with an average diameter of $27.0 \pm 6.5$ nm retain the bulk-like two-step antiferromagnetic transitions, as shown by magnetization and heat-capacity measurements. Below the lower transition, the nanocrystals exhibit a hysteretic ferromagnetic response with large coercivity, exchange bias, and a vertical loop shift after field cooling, whereas the $M$-$H$ response just above the transition is nearly linear. These features are best explained by uncompensated surface moments generated where the low-temperature antiferromagnetic order terminates at the nanocrystal surface. The absence of a clear additional bulk-like weak-ferromagnetic component constrains homogeneous-canting models and indirectly favors a domain-wall scenario for the weak ferromagnetism of bulk NiS$_2$.

cond-mat.str-el↗

arXiv2026

Robust Metal-Insulator Transition Despite Surface Dead-Layer Growth in Sub-10-nm Cr-Doped V2O3 Nanocrystals

We investigated the size dependence of the metal-insulator transition (MIT) in Cr-doped V2O3 nanocrystals by photoemission spectroscopy using complementary probing depths, together with magnetic susceptibility measurements. Photoemission spectra show that MIT signatures persist down to an average particle size of 5.6 nm, and magnetic susceptibility measurements exhibit a nearly size-invariant transition onset. The contrast between surface-sensitive and deeper-probing photoemission spectra reveals that the transition survives in the nanocrystal interior. At the same time, the spectra indicate a systematic suppression of coherent quasiparticle weight with decreasing size, pointing to the growth of an insulating surface dead layer. These results demonstrate that nanoscaling does not intrinsically eliminate the MIT itself, but progressively enhances the influence of surface-driven insulating behavior, thereby providing insight into the practical limits of miniaturizing Mott-based devices.

cond-mat.str-el↗

arXiv2020

Stabilization of Nonmagnetic Hexagonal Close-Packed Phase in Nanocrystalline Nickel Metal with a Giant Volume Expansion

Nanocrystalline Ni can adopt a hexagonal close-packed (hcp) structure,which does not appear in a bulk form under any conditions.Structural studies found its $>$ 20% expansion of volume per atom compared with face-centered cubic (fcc) Ni.Hard x-ray photoemission spectroscopy of the hcp phase revealed a $>$ 0.14 valence electron transfer from 3$d$ to 4$s$ and 4$p$ orbitals and a 0.25 eV reduction in band energy per electron compared with the fcc phase.Its nonmagnetic nature was attributed to a low density of states at the Fermi level.Thermodynamic stability of the hcp phase can be explained by the band energy gain and the electrostatic potential energy loss as related to the large lattice expansion.

cond-mat.mtrl-sci↗