Electric transport as a probe to unveil microscopic aspects of oxygen-depleted YBCO
We report on the characterization of Pt-YBa$_2$Cu$_3$O$_{7-δ}$ interfaces, focusing on how oxygen vacancies content ($δ$) affects electrical transport mechanisms. Our study examines four Pt-YBa$_2$Cu$_3$O$_{7-δ}$ samples with varying $δ$ (0.12 $\leq δ\leq$ 0.56) using voltage-current measurements across a temperature range. We successfully model the electrical behavior using a Poole-Frenkel conduction framework, revealing that oxygen vacancies create potential wells that trap carriers, directly influencing conduction. We observe that the energy of these traps increases as $δ$ rises, in agreement with a peak previously detected in optical conductivity measurements. This result supports earlier interpretations, strengthening the proposed connection between oxygen vacancies and the ionization energy associated with impurity bands in YBa$_2$Cu$_3$O$_{7-δ}$.