arXiv2003

Ultrafast collective dynamics of short-range charge/orbital ordering fluctuations in colossal magnetoresistive oxides

The "colossal magnetoresistive" (CMR) manganites are highly correlated systems with a strong coupling between spin, charge, orbital, and lattice degrees of freedom, which leads to complex phase diagrams and to the coexistence of various forms of ordering. For example, nanoscale charge/orbital ordering (CO) fluctuations appear to cooperate with Jahn-Teller (JT) distortions of the MnO$_{6} octahedra in CMR manganites and compete with the electron itinerancy favored by double exchange. However, access to the ordered dynamical state has been challenging, mostly due to intrinsic experimental difficulties in measuring fast short-range correlations. Here, we report on a strongly damped low-energy collective mode originating from fast short-range CO fluctuations in La}$_{0.67}Ca$_{0.33}Mn{O}$_{3}(LCMO) single crystal and thin films. We elucidate the collective mode in terms of its dispersion relation and dependence on average A-site ion radius, r$_{A}, and hole-doping concentration. Our results show for the first time that dynamical short-range CO correlations in CMR manganites can be detected with high momentum resolution by coherent ultrafast optical techniques.

cond-mat.str-el↗

arXiv2002

Coupling parameter in synchronization of diluted neural networks

We study the critical features of coupling parameter in the synchronization of neural networks with diluted synapses. Based on simulations, the exponential decay form is observed in the extreme case of global coupling among subsystems and fully linking in each network: there exists maximum and minimum of the critical coupling intensity for synchronization in this spatially extended system. For the partial coupling, we present the primary result about the critical coupling fraction for various linking degrees of networks.

cond-mat.dis-nn↗

arXiv2002

In situ epitaxial MgB2 thin films for superconducting electronics

A thin film technology compatible with multilayer device fabrication is critical for exploring the potential of the 39-K superconductor magnesium diboride for superconducting electronics. Using a Hybrid Physical-Chemical Vapor Deposition (HPCVD) process, it is shown that the high Mg vapor pressure necessary to keep the MgB$_2$ phase thermodynamically stable can be achieved for the {\it in situ} growth of MgB$_2$ thin films. The films grow epitaxially on (0001) sapphire and (0001) 4H-SiC substrates and show a bulk-like $T_c$ of 39 K, a $J_c$(4.2K) of $1.2 \times 10^7$ A/cm$^2$ in zero field, and a $H_{c2}(0)$ of 29.2 T in parallel magnetic field. The surface is smooth with a root-mean-square roughness of 2.5 nm for MgB$_2$ films on SiC. This deposition method opens tremendous opportunities for superconducting electronics using MgB$_2$.

cond-mat.mtrl-sci↗

arXiv2001

Superconducting properties of nanocrystalline MgB$_2$ thin films made by an in situ annealing process

We have studied the structural and superconducting properties of MgB$_2$ thin films made by pulsed laser deposition followed by in situ annealing. The cross-sectional transmission electron microscopy reveals a nanocrystalline mixture of textured MgO and MgB$_2$ with very small grain sizes. A zero-resistance transition temperature ($T_{c0}$) of 34 K and a zero-field critical current density ($J_c$) of $1.3 \times 10^6$ A/cm$^2$ were obtained. The irreversibility field was $\sim$ 8 T at low temperatures, although severe pinning instability was observed. These bulk-like superconducting properties show that the in situ deposition process can be a viable candidate for MgB$_2$ Josephson junction technologies.

cond-mat.mtrl-sci↗

arXiv2001

Thermodynamics of the Mg-B system: Implications for the deposition of MgB2 thin films

We have studied thermodynamics of the Mg-B system with the modeling technique CALPHAD using a computerized optimization procedure. Temperature-composition, pressure-composition, and pressure-temperature phase diagrams under different conditions are obtained. The results provide helpful insights into appropriate processing conditions for thin films of the superconducting phase, MgB2, including the identification of the pressure/temperature region for adsorption-controlled growth. Due to the high volatility of Mg, MgB2 is thermodynamically stable only under fairly high Mg overpressures for likely growth temperatures. This constraint places severe temperature constraints on deposition techniques employing high vacuum conditions.

cond-mat.mtrl-sci↗