Illuminating early ZrC oxidation using ensemble small-cell DFT with dynamic gas management
During zirconium carbide oxidation, liberated carbon can remain beneath the oxide or escape as gas, complicating the interpretation of mass measurements. We adapt the small-cell ensemble method using sixteen 140 ps ab initio molecular dynamics trajectories at 873-1273 K under a sustained high oxygen flux with gas removal. The average rates of net mass gain and total carbon transfer into gas or retained chains follow Arrhenius trends. Above 973 K, gas evolution levels off while total carbon transfer increases. The fraction of transferred carbon retained in chains rises from 40 % at 973 K to 66 % at 1273 K. Fits after 40 ps suggest declining carbon transfer rates over time, although not in every trajectory. These results show that carbon partitioning during early oxidation depends on temperature, with increasing temperature above 973 K favouring chain formation over gasification.