Pressure-Induced Irreversible Disorder in $\beta^{\prime}$-Mn$_3$(PO$_4$)$_2$: A High-Pressure X-ray Diffraction and Density-Functional Theory Study

The high-pressure structural behavior of $\beta^\prime$-Mn$_3$(PO$_4$)$_2$ was investigated using synchrotron X-ray diffraction up to 20 GPa combined with density-functional theory calculations. At ambient conditions, $\beta^\prime$-Mn$_3$(PO$_4$)$_2$ crystallizes in a monoclinic structure that exhibits strongly anisotropic compression. The pressure dependence of the unit-cell volume was described using a third-order Birch--Murnaghan equation of state, and the principal axes of compressibility were determined. Above 14.1 GPa, significant broadening and weakening of the diffraction peaks are attributed to the onset of irreversible pressure-induced structural disorder associated with the loss of long-range crystallographic order. The disordered state persists after decompression to ambient pressure, demonstrating the irreversible nature of the transformation. The calculations accurately reproduce the experimental compressional behavior and provide insights into the microscopic structural evolution under pressure. Compression is mainly accommodated through distortions of the Mn--O polyhedra, whereas the PO$_4$ tetrahedra behave as comparatively rigid units. Several initially penta-coordinated Mn sites progressively evolve toward octahedral coordination under compression, while selected MnO$_6$ polyhedra exhibit anomalous distortions and elastic softening preceding the onset of disorder. Elastic constant calculations further reveal that the crystalline phase becomes mechanically unstable near the experimentally observed transition pressure. The combined experimental and computational results suggest that the HP response of $\beta^\prime$-Mn$_3$(PO$_4$)$_2$ is influenced by the interplay between framework complexity, anisotropic polyhedral compressibility, and elastic instability, providing new insight into pressure-induced structural degradation in structurally complex phosphate frameworks.

cond-mat.mtrl-sci

High-Pressure Structural Evolution of Na2ZrSi2O7 and Na2ZrSi2O7.H2O: Topology-Driven Compression Behaviors, Phase Stability, and Electronic Transitions

Silicate frameworks exhibit diverse structural responses under extreme conditions, which are strongly influenced by hydration. Here, we present a comparative high-pressure synchrotron X-ray diffraction study of Na2ZrSi2O7 and its hydrated analogue Na2ZrSi2O7.H2O up to 30 GPa, combined with electronic structure calculations. At ambient conditions, both phases share the same primary building units (PBUs: [ZrO6] and [SiO4]) but differ in secondary building units (SBUs, M2T4 vs. M2T6). Under compression, Na2ZrSi2O7 undergoes a phase transition near 15 GPa, while the hydrated phase remains stable throughout the pressure range. The anhydrous compound exhibits a higher bulk modulus (B0 = 77.1 GPa) and less anisotropic compression compared with the hydrated phase (B0 = 66.3 GPa). Distinct deformation mechanisms are observed: the anhydrous framework accommodates pressure through [ZrO6] octahedral distortion, whereas the hydrated framework compresses via [Si2O7] group tilting. Electronic structure calculations indicate band gap widening with pressure in both phases; notably, Na2ZrSi2O7 shows a direct-to-indirect band gap transition, whereas the hydrated phase retains a direct gap. These results reveal how hydration-driven topological modifications at the secondary building unit scale dictate the pressure-induced structural evolution, phase stability, and electronic properties of zirconosilicate frameworks.

cond-mat.mtrl-sci

Effects of Compression on the Local Iodine Environment in Dipotassium Zinc Tetraiodate(V) Dihydrate K2Zn(IO3)4.2H2O

Combining X-ray diffraction with density-functional theory and electron topology calculations we found that pressure substantially modifies the bonding in K2Zn(IO3)4.2H2O. We discovered that under compression there is a progressive change from primary covalent I-O bonds and secondary halogen I-O interactions towards O-I-O electron-deficient multicenter bonds. Because of this, iodine hypercoordination converts IO3 trigonal pyramids towards IO6 units. The formation of these IO6 units breaks the typical isolation of iodate molecules forming an infinite two-dimensional iodate network. Hypercoordination influences the hydrogen atoms too, such that multicenter O-H-O bonds are also promoted with increasing pressure. We have determined that K2Zn(IO3)4.2H2O is one of the most compressible iodates studied to date, with a bulk modulus of 22(3) GPa. The pressure-induced structural changes strongly modify the electronic structure as shown by optical-absorption measurements and band-structure calculations. The band-gap energy closes from 4.2(1) eV at ambient pressure to 3.4(1) eV at 20 GPa.

cond-mat.mtrl-sci

The effect of pressure in the crystal and magnetic structure of FeWO4

The temperature dependence of the structural and magnetic properties of wolframite-type FeWO4 were studied in situ by high pressure neutron diffraction. Neutron diffraction measurements were performed at the XtremeD instrument at the Institut Laue Langevin up to a maximum pressure of 8.7(4) GPa and a minimum temperature of 30.0(5) K. The diffraction data were analyzed via Rietveld refinements. We found that despite of producing a contraction of 5% of the volume, the maximum pressure applied in this study does not modify the Shubnikov space group below magnetic order. However, the orientation of magnetic moments and the N\'eel temperature, are slightly modified with the pressure, which is expected according to the preexistent understanding of magnetism in wolframites. We also determined a pressure-volume equation of state of FeWO4 at 300 K, which is compared with previous X-ray diffraction studies and density-functional theory calculations.

cond-mat.mtrl-sci

High-Pressure X-Ray Diffraction Study of Scheelite-type Perrhenates

The effects of pressure on the crystal structure of scheelite-type perrhenates were studied using synchrotron powder X-ray diffraction and density-functional theory. At ambient conditions, the studied materials AgReO4, KReO4, and RbReO4, exhibit a tetragonal scheelite-type crystal structure described by space group I41/a. Under compression, a transition from scheelite-to-M${\prime}$-fergusonite (space group P21/c) was observed at 1.6 and 7.4 GPa for RbReO4 and KReO4, respectively. The transition involves a relative volume decrease. On the other hand, AgReO4 underwent a phase transition to the M-fergusonite structure (space group I2/a) at 13.6 GPa. In this case there is no appreciable volume discontinuity. The room-temperature pressure-volume equation of state for the three studied perrhenates was estimated using a second-order Birch-Murnaghan equation of state. The results for the low-pressure phase are confirmed by density-functional theory calculations. The analysis of the bulk modulus shows that the compressibility of the compounds decreases following the sequence RbReO4 > KReO4 > AgReO4, which is related to the compressibility of the RbO8, KO8, and AgO8 bidisphenoid units. Density-functional theory also offers valuable insights into the elastic constants. Despite giving a good description for the low-pressure phase in the three compounds, density-functional theory cannot catch the structural phase transition observed in experiments. Reasons for it are discussed in the manuscript.

cond-mat.mtrl-sci

Identification of the high-pressure phases of alpha-SnWO4 combining x-ray diffraction and crystal structure prediction

We have characterized the high-pressure behavior of alpha-SnWO4. The compound has been studied up to 30 GPa using a diamond-anvil cell and synchrotron powder X-ray diffraction. We report evidence of two structural phase transitions in the pressure range covered in our study, and we propose a crystal structure for the two high-pressure phases. The first one, observed around 12.9 GPa, has been obtained combining indexation using DICVOL and density-functional theory calculations. The second high-pressure phase, observed around 17.5 GPa, has been determined by using the CALYPSO code, the prediction of which was supported by a Le Bail fit to the experimental X-ray diffraction patterns. The proposed structural sequence involves two successive collapses of the unit-cell volume and an increase in the coordination number of Sn and W atoms. The room-temperature equations of state, the principal axes of compression and their compressibility, the elastic constants, and the elastic moduli are reported for {\alpha}-SnWO4 and for the two high-pressure phases.

cond-mat.mtrl-sci

Pressure-Induced Decomposition of beta-SnWO4

This study reports the decomposition of beta-SnWO4 into Sn, SnO2, and WO3 induced by static compression. We performed high-pressure synchrotron powder angle-dispersive X-ray diffraction measurements and found that decomposition occurs at a pressure of 13.97(5) GPa and is irreversible. This result contradicts a previous study that, based on density-functional theory calculations and crystal-chemistry arguments, predicted a pressure-driven transition from beta-SnWO4 to alpha-SnWO4. Our analysis indicates that the observed decomposition is unrelated to mechanical or dynamic instabilities. Instead, it likely stems from frustration of the beta-alpha transition, as this transformation requires a change in Sn coordination from octahedral to tetrahedral. The assessment of how pressure influences the volume of the unit cell provided an accurate determination of the room-temperature pressure-volume equation of state for beta-SnWO4. Furthermore, the elastic constants and moduli, as well as the pressure dependence of Raman and infrared modes of beta-SnWO4, were derived from density-functional theory calculations. Several phonon modes exhibited softening, and three cases of phonon anti-crossing were observed.

cond-mat.mtrl-sci