arXiv2018

Low temperature magnetic properties of Nd2Ru2O7

We present magnetic susceptibility, heat capacity, and neutron diffraction measurements of polycrystalline Nd2Ru2O7 down to 0.4 K. Three anomalies in the magnetic susceptibility measurements at 146, 21 and 1.8 K are associated with an antiferromagnetic ordering of the Ru4+ moments, a weak ferromagnetic signal attributed to a canting of the Ru4+ and Nd3+ moments, and a long-range-ordering of the Nd3+ moments, respectively. The long-range order of the Nd3+ moments was observed in all the measurements, indicating that the ground state of the compound is not a spin glass. The magnetic entropy of Rln2 accumulated up to 5 K, suggests the Nd3+ has a doublet ground state. Lattice distortions accompany the transitions, as revealed by neutron diffraction measurements, and in agreement with earlier synchrotron x-ray studies. The magnetic moment of the Nd3+ ion at 0.4 K is estimated to be 1.54(2)μB and the magnetic structure is all-in all-out as determined by our neutron diffraction measurements.

cond-mat.str-el↗

arXiv2006

Paramagnetism of the Co sublattice in ferromagnetic Zn$_{1-x}$Co$_{x}$O films

Using the spectroscopies based upon x-ray absorption, we have studied the structural and magnetic properties of Zn$_{1-x}$Co$_{x}$O films ($x$ = 0.1 and 0.25) produced by reactive magnetron sputtering. These films show ferromagnetism with a Curie temperature $T_{\mathrm{C}}$ above room temperature in bulk magnetization measurements. Our results show that the Co atoms are in a divalent state and in tetrahedral coordination, thus substituting Zn in the wurtzite-type structure of ZnO. However, x-ray magnetic circular dichroism at the Co \textit{L}$_{2,3}$ edges reveals that the Co 3\textit{d} sublattice is paramagnetic at all temperatures down to 2 K, both at the surface and in the bulk of the films. The Co 3\textit{d} magnetic moment at room temperature is considerably smaller than that inferred from bulk magnetisation measurements, suggesting that the Co 3\textit{d} electrons are not directly at the origin of the observed ferromagnetism.

cond-mat.mtrl-sci↗