Phase diagram analysis and crystal growth of solid solutions Ca_{1-x}Sr_xF_2
The binary phase diagram CaF$_2$--SrF$_2$ was investigated by differential thermal analysis (DTA). Both substances exhibit unlimited mutual solubility with an azeotropic point showing a minimum melting temperature of T_\mathrm{min}=1373^{\circ}$C for the composition Ca$_{0.582}$Sr$_{0.418}$F$_2$. Close to this composition, homogeneous single crystals up to 30 mm diameter without remarkable segregation could be grown by the Czochralski method.
cond-mat.mtrl-sci↗