Competing effects of Si and Mg doping on native point defects in yttrium aluminum garnet
We investigate how Si and Mg doping affect native point defects in yttrium aluminum garnet (YAG) by combining first-principles calculations with a thermodynamic model of defect equilibria. Formation energies and equilibrium concentrations of native defects, dopants, and defect complexes are obtained across the full range of oxygen chemical potentials relevant to ceramic sintering. Donor (Si) and acceptor (Mg) dopants are found to control native defect populations efficiently but in opposite directions: Si substantially raises cation-vacancy concentrations while suppressing oxygen vacancies, whereas Mg produces the reverse trend. Depending on dopant concentration and oxygen chemical potential, native vacancy concentrations vary by up to thirteen orders of magnitude. The concentration of isolated cation vacancies depends nonmonotonically on Si content, a consequence of Si-vacancy complex formation. Under Si-Mg co-doping, the two dopants compensate each other efficiently, giving rise to pronounced minima in both cation- and oxygen-vacancy concentrations when Si and Mg are present in equal amounts. These findings provide a microscopic basis for the pronounced sensitivity of YAG sintering behavior to the Si/Mg ratio, and show that balanced donor-acceptor co-doping is an effective strategy for controlling native defect populations in YAG.