arXiv2026

Effects of high-pressure synthesis on phase formation and superconducting properties of PrFeAsO1-xFx

Motivated by recent reports of enhanced superconducting performance in several families of iron-based superconductors (IBS) processed by high-pressure (HP) synthesis, we investigate the influence of high gas pressure and high-temperature synthesis (HP-HTS) process on the structural, microstructural, electrical transport, and magnetic properties of Pr-based oxypnictide PrFeAsO1-xFx (Pr1111) using the processing conditions of 0.5 GPa for 1 h previously optimized for other IBS families. Representative underdoped (x = 0.2), optimal doped (x = 0.3), and overdoped (x = 0.5) compositions from the ambient-pressure electronic phase diagram of Pr1111 are selected to evaluate its composition-dependent effects of HP-HTS. The results demonstrate that HP-HTS enhances fluorine incorporation, improves phase formation, and produces a denser microstructure with improved grain connectivity in the underdoped and optimal doped compositions. Magnetic measurements reveal increased in the superconducting transition temperature (Tc) of ~1 K for x = 0.2 and ~6 K for x = 0.3, whereas only a marginal improvement in the critical current density is observed. Electrical resistivity measurements of the underdoped composition show a slight increase in Tc accompanied by a broader resistive transition, indicating residual structural inhomogeneity. In contrast, the overdoped composition exhibits increased impurity phase segregation, accompanied by suppression of superconductivity. These results demonstrate that the effectiveness of HP-HTS in Pr1111 is strongly composition dependent and governed by the interplay among fluorine incorporation, phase stability, and microstructural evolution, highlighting the need for further optimization of the HP-HTS processing conditions.

cond-mat.supr-con↗

arXiv2025

Synthesis and characterizations of arsenic doped FeSe bulks

FeSe(11) family has a simple crystal structure belonging to iron-based superconductors (FBS) and has many stable phases including hexagonal and tetragonal structures, but only the tetragonal phase exhibits the superconductivity. In this study, we have investigated the effects of chemical pressure induced by As-doping at Se-sites in the FeSe system by preparing a series of FeSe1-xAsx (x = 0.005, 0.01, 0.02, 0.05, 0.1, and 0.2) bulks. A broad characterization has been performed on these samples using structural, microstructural, transport, and magnetic measurements. The obtained lattice parameters are increased by As-doping, which suggests the successful insertion of As at Se-sites into the tetragonal lattice for low doping contents up to 5%, whereas the higher As-substitution appears in the form of the FeAs impurity phase. The temperature dependence of the resistivity of all samples has similar behaviour and depicts the highest onset transition temperature of around 11.5 K, but the zero resistivity is not reached until the measured temperature of 7 K, which could be due to the presence of the impurity phases. Our study suggests that a dopant with a large ionic radius, i.e., Arsenic, promotes the formation of the hexagonal phase of the 11 family and is effective for a small amount of doping level for the superconducting properties, whereas higher As-doping levels reduce the superconducting properties.

cond-mat.supr-con↗

arXiv2024

Praseodymium doping effect on the superconducting properties of FeSe$_{0.5}$Te$_{0.5}$ bulks under ambient and high-pressure growth conditions

A series of Pr-doped FeSe$_{0.5}$Te$_{0.5}$ (Fe$_{1-x}$Pr$_x$Se$_{0.5}$Te$_{0.5}$; $x = 0$ to 0.3) bulks are prepared by conventional synthesis process at ambient pressure (CSP), and high gas pressure and high temperature synthesis (HP-HTS) methods. These bulks are well characterized by structural and microstructural analysis, Raman spectroscopy, transport, and magnetic measurements. The HP-HTS process of the parent bulks has enhanced the onset transition temperature ($T_c^{\rm onset}$) by 1.5 K and the critical current density ($J_c$) by two orders of magnitude compared to the CSP method. Pr-doped FeSe$_{0.5}$Te$_{0.5}$ up to 10% doping content prepared, either CSP or HP-HTS, slightly increases the unit cell volume, and high-pressure growth produces an almost pure superconducting phase, which confirms the successful Pr-doping at Fe sites. Raman spectroscopy measurements and DFT calculations suggest the substitution of Pr-atoms in the interlayer spacing of Fe(Se,Te) lattice. High-pressure growth of Fe$_{1-x}$Pr$_x$Se$_{0.5}$Te$_{0.5}$ also makes the sample less dense compared to the parent sample grown by HP-HTS. Transport and magnetic measurements depict that Tconset is almost unaffected by Pr-doping, whereas $J_c$ of Pr-doped FeSe$_{0.5}$Te$_{0.5}$ is enhanced by one order of magnitude relative to the parent sample developed by CSP but lower than that of the parent sample grown by HP-HTS. Hence, Pr-doping at Fe sites preserves $T_c^{\rm onset}$ and improves $J_c$ of FeSe$_{0.5}$Te$_{0.5}$ regardless of the doping contents and growth conditions. These results are promising for the practical application of iron-based superconductors to improve $J_c$ properties without affecting $T_c^{\rm onset}$ through CSP process and congruent with discoveries from other superconductors, like cuprates and MgB$_2$.

cond-mat.supr-con↗

arXiv2023

Comparison of Gd addition effect on the superconducting properties of FeSe0.5Te0.5 bulks under ambient and high-pressure conditions

We have prepared a series of (FeSe0.5Te0.5 + xGd) bulk samples, with x = 0, 0.03, 0.05, 0.07, 0.1 and 0.2, through the convenient solid-state reaction method at ambient pressure (CSP). High gas pressure and high-temperature synthesis methods (HP-HTS) are also applied to grow the parent compound (x = 0) and 5-wt% of Gd-added bulks. Structural, microstructural, transport and magnetic characterizations have been performed on these samples in order to draw the final conclusion. Our analysis results that the HP-HTS applied for the parent compound enhances the transition temperature (Tc) and the critical current density (Jc) with the improved sample density and intergrain connections. The lattice parameter c is increased with Gd additions, suggesting a small amount of Gd enters the tetragonal lattice of FeSe0.5Te0.5 and the Gd interstitial sites are along the c-axis. A systematic decrease of the onset transition temperature Tc is observed with Gd additions, however, the calculated Jc of these Gd-added samples is almost the same as that of the parent compound prepared by CSP. It specifies that there is no improvement of the grain connections or pinning properties due to these rare earth additions. However, Gd-added FeSe0.5Te0.5 bulks prepared by HP-HTS have revealed a slightly improved critical current density due to improved grain connections and sample density but have a lower transition temperature than that of the parent compounds.