Magnetic order in epitaxial (La2/3Sr1/3MnO3)3/(BaTiO3)3 trilayer heterostructures
The realization of artificial magnetic structures with high epitaxial quality and elevated critical temperatures remains a key challenge for spintronics. Here, we report the fabrication and characterization of epitaxial (La2/3Sr1/3MnO3)3/(BaTiO3)3 trilayer heterostructures grown by layer-by-layer laser ablation. High-resolution transmission electron microscopy, magnetization measurements, and neutron diffraction confirm their exceptional crystalline order and the absence of structural defects. Neutron diffraction reveals no antiferromagnetic at non-zero wavevector Bragg peaks, ruling out most antiferromagnetic configurations with a non zero wave vector Q. Magnetic hysteresis loops instead evidence a ferromagnetic order with a remanent moment of about 0.5 Bohr magneton per Mn atom at room temperature, persisting either in-plane or out-of-plane depending on the applied field. Our findings highlight neutron diffraction as a powerful tool for elucidating the magnetic structure of complex thin films and suggest that weak interlayer coupling through BaTiO3 leads to ferromagnetism with a high critical temperature (about 600 K).