arXiv2025

Segregation-driven cross-slip mechanism of shockley partials in the gamma prime phase of CoNi-based superalloys

In general, the cross-slip of superdislocations (a/2<011>) from {111} planes to {001} planes has been frequently observed in superalloys, accompanied by the formation of an antiphase boundary (APB) and driven by thermal activation. However, no prior studies have evidenced the occurrence of Shockley partial dislocation (a/6<112>) cross-slip within the gamma prime phase of superalloys. In this work, we present a newly observed cross-slip phenomenon: the Shockley partial dislocations cross-slip from one {111} plane to another {111} conjugate plane, facilitated by the formation of a stair-rod dislocation in the ordered gamma prime phase of a CoNi-based superalloy. Compression tests were conducted at 850 degrees Celsius with a strain rate of 10^-4 s^-1. Defects such as stacking faults and dislocations, along with the associated chemical fluctuations, were characterized using high-resolution scanning transmission electron microscopy (HRSTEM) and energy-dispersive X-ray spectroscopy (EDS). Elemental segregation was found to reduce the activation energy required for cross-slip by decreasing the energies of stacking faults and dislocations. In addition to elemental segregation, local stress concentrations, arising from the combined effects of applied stress, shearing dislocations within the gamma prime phase, and dislocation pile-ups, also play a critical role in triggering cross-slip. The formation of sessile stair-rod dislocations via this newly identified Shockley partial cross-slip in the gamma prime phase is beneficial for enhancing the high-temperature deformation resistance of the alloy by increasing the critical resolved shear stress required for further plastic deformation.

cond-mat.mtrl-sci↗

arXiv2024

High-Ti induced planar-fault transformation toward superlattice extrinsic stacking faults and microtwins in crept CoNi-based superalloys

Controlling planar fault shearing mechanisms is key for improving the high-temperature creep performance of gamma prime-strengthened high-temperature superalloys. This work examines how the Ti concentration in L12-strengthened CoNi-based alloys affects planar fault formation during creep. Interrupted compressive creep tests were conducted at 1223 K under air with a constant load stress of 241 MPa. We found, for the first time, that high Ti additions shift the dominant gamma prime shearing mode from antiphase boundaries (APBs) in Ti-free and low-Ti alloys to superlattice extrinsic stacking faults (SESFs). Systematic ab initio calculations show that in high-Ti alloys, the elevated APB energy renders APB-shearing mode unfavorable. Nevertheless, the SESF energy decreases relative to that in low-Ti compositions, and an increased ratio of complex intrinsic stacking fault (CISF) to SESF energy promote the transformation of high-energy CISFs into lower-energy SESFs. Chemical analysis using scanning transmission electron microscopy combined with energy-dispersive X-ray spectroscopy further reveals that, SESFs in high-Ti alloys are enriched in Ti, Mo and W, yet no grid-like ordering is observed. Together with the ab initio calculations, Mo and W additions in high Ti alloys could facilitate the transformation from L12 structure to low-energy D024 structure, indicating Mo and W segregation along SESFs is energetically favourable. Furthermore, the successive SESF thickening facilitates microtwinning in the absence of D024 ordering along SESFs, as an additional big carrier for creep strain. These new findings clarify the role of Ti in controlling planar fault shearing mechanisms, providing new insights for optimizing the creep performance of next-generation CoNi-based superalloys.

cond-mat.mtrl-sci↗

arXiv2024

Extreme high lattice-misfit superalloys with regular cubic L12 particles and excellent creep resistance

In novel Co and CoNi based superalloys, the creep resistance is limited at high temperatures due to low lattice misfit and solvus temperature. In this study, we combined the advantages of Co-Ti (high lattice misfit and solvus temperature) and Co-Al based superalloys (cuboidal precipitates) by using Ti to substitute Al in alloys of Co-30Ni-(12.5-x)Al-xTi-2.5Mo-2.5W (at.%) composition. With high Ti content, the alloys obtained extreme high lattice misfit (bigger than 1.3 %) and solvus temperature (bigger than 1150 degree). During aging at 900 degree, alloys with high Ti/Al ratio exhibited a lower gamma prime precipitate coarsening rate resulting from their lower gamma prime and gamma interfacial energy and higher lattice misfit. In addition, high Ti/Al ratio brought higher gamma prime volume fraction and excellent mechanical properties, such as higher yield stress and better creep resistance. However, at high temperature of 1100 degree, the cubic gamma prime phase was decomposed into deleterious Eta phase with D024 structure if the Ti/Al ratio exceeded 1. Based on this, we outreached new alloys design with a high content of Cr and Ta and appropriate Ti/Al ratio, i.e., Ti/Al ratio is smaller than 1. The newly designed alloys still have high solvus temperature (bigger than 1200 degree) and exhibit high lattice misfit (bigger than 1.2 %) as Co-12Ti (at.%) superalloys but more regular cubic gamma prime precipitates and significantly better creep resistance than superalloys Co-9Al-9W and Co-9Al-9W-2Ti at 850 and 950 degree. Nevertheless, compared with creep resistance of Ni based superalloys, our newly designed alloys still need to be further improved, especially in the 1000 and 1050 degree range.

cond-mat.mtrl-sci↗

arXiv2024

Crystal rotation during alloy heating

Over past decades, high energy X-ray diffraction techniques at synchrotron beamline offer us the unique possibility to follow concomitantly some mechanisms on the grain level in metallic materials. Crystal rotation, as one important factor for the crystal orientation distribution, usually influences the anisotropic properties of materials. Crystal rotation has been visualized in deformation, recrystallization, and chemical reaction processes. In this study, we firstly visualized an unexpected crystal rotation during heating up of superalloys as well by in situ 3DXRD scanning microscopy which has not been previously reported yet. The crystal rotation was found to be related to the locked-in first order residual strain relief during the annealing treatment. In addition, intermittent dynamic, i.e., some individual diffraction spots from Debye-Scherrer rings appearing, disappearing, and reappearing, occurred in this study which has ever been thought to be caused by subgrain formation in deformation experiments. However, by residual strain analysis coupled with finite element simulation, we found that the intermittent dynamic is married with thermal expansion, crystal distortion, and crystal rotation as well. This finding opens a new world for deeply understanding the residual strain relief during materials, particularly metal, heating.

cond-mat.mtrl-sci↗

arXiv2024

Vacancies making jerky flow in complex alloys

Longevity of materials, especially alloys, is crucial for enhancing the sustainability and efficiency of various applications, including gas turbines. Jerky flow, also known as dynamic strain aging effect, can indeed have a significant impact on the fatigue life of high-temperature components in gas turbines. In general, three jerky flow types, i.e., A, B and C, existed in superalloys. Type A and B, occurring at low temperature, were proved to be caused by interstitial elements, such as carbon. However, Type C serration at high temperature has not been verified directly and remains unresolved, which was unanimously agreed it is caused by the interaction between solute elements and dislocations. In this study, our new discovery challenged this mainstream axiom. We proposed that vacancies play a dominant role in inducing jerky flow instead of solute atoms. By transmission electron microscopy, we observed directly that dislocations are pinned by vacancy-type dislocation loops (PDLs) or dipoles. Our findings suggest that vacancies located at dislocation jogs are primarily responsible for pinning and unpinning of superlattice dislocations. As dislocations move and interact with vacancies, PDLs or dipoles are left behind in their path. This pinning and unpinning process is repeated as successive dislocations encounter the newly formed PDLs or dipoles, leading to the recurring fluctuations in the stress, i.e., serrated flow. Additionally, antisite defects created by Co, Cr and Ti sitting on Ni positions is postulated to facilitate vacancy formation and migration towards dislocations via nearest neighbor jumps. This study provides a new avenue to show how future alloy design can improve the fatigue life of superalloys in extreme environments.

cond-mat.mtrl-sci↗

arXiv2020

Amorphous Mo-Ta oxide nanotubes for long-term stable Mo oxide based supercapacitors

With a large-scale usage of portable electric appliances, a high demand for increasingly high density energy storage devices has emerged. MoO3 has, in principle, a large potential as negative electrode material in supercapacitive devices, due to high charge densities that can be obtained from its reversible redox reactions. Nevertheless, the extremely poor electrochemical stability of MoO3 in aqueous electrolytes prevents a practical use in high capacitance devices. In this work, we describe how to overcome this severe stability issue by forming amorphous molybdenum oxide/tantalum oxide nanotubes by anodic oxidation of a Mo-Ta alloy. The presence of a critical amount of Ta-oxide (> 20 at-%) prevents the electrochemical decay of the MoO3 phase and thus yields an extremely high stability. Due to the protection provided by tantalum oxide, no capacitance losses are measureable after 10000 charg-ing/discharging cycles.

physics.app-ph↗