Origin of circular and triangular pores in electron-irradiated hexagonal boron nitride

For nearly two decades, it has been known that electron irradiation of hexagonal boron nitride (hBN) in a transmission electron microscope leads to the formation of triangular pores. This has been attributed to the lower displacement threshold energy of boron, with or without the assistance of an inelastic scattering event, typically assuming that chemical processes caused by residual gases can be neglected. In this study, in contrast to previous high-vacuum experiments, we show that electron irradiation in ultra-high vacuum leads to circular pores, whereas even small amounts of oxygen in the atmosphere during the experiment drive the pores to grow into triangle shapes with nitrogen-terminated edges. This result is shown to hold for samples of different types and from different manufacturers, and at different electron energies as well as focused scanning and defocused stationary beams. Our results explain the chemical origin of triangular pores in hBN and demonstrate a deterministic way to create atomically defined pores in this important 2D material.

cond-mat.mtrl-sci↗

arXiv2025

Single photon emitters in hBN: Limitations of atomic resolution imaging and potential sources of error

There is a growing interest in identifying the origin of single-photon emission in hexagonal boron nitride (hBN), with proposed candidates including boron and nitrogen vacancies as well as carbon substitutional dopants. Because photon emission intensity often increases with sample thickness, hBN flakes used in these studies commonly exceed 30 atomic layers. To identify potential emitters at the atomic scale, annular dark-field scanning transmission electron microscopy (ADF-STEM) is frequently employed. However, due to the intrinsic AA' stacking of hBN with vertically alternating boron and nitrogen atoms, this approach is complicated even in few-layer systems. Here, we demonstrate using STEM image simulations and experiments that, even under idealized conditions, the intensity differences between boron- and nitrogen-dominated columns and carbon substitutions become indistinguishable at thicknesses beyond 17 atomic layers (ca. 6 nm). While vacancy-type defects can remain detectable at somewhat larger thicknesses, also their detection becomes unreliable at thicknesses typically used in photonic studies. We further show that common residual aberrations, particularly threefold astigmatism, can lead to artificial contrast differences between columns, which may result in misidentification of atomic defects. We systematically study the effects of non-radially symmetric aberrations on multilayer hBN and demonstrate that even small residual threefold astigmatism can significantly distort the STEM contrast, leading to misleading interpretations.

cond-mat.mtrl-sci↗