arXiv2024

Tuning chemical short-range order for stainless behavior at reduced chromium concentrations in multi-principal element alloys

Single-phase multi-principal element alloys (MPEAs) hold promise for improved mechanical properties as a result of multiple operative deformation modes. However, the use of many of these alloys in structural applications is limited as a consequence of their poor aqueous corrosion resistance. Here we introduce a new approach for significantly improving the passivation behavior of alloys by tuning the chemical short-range order (CSRO) parameter. We show that the addition of only 0.03 to 0.06 mole fraction of Al to a (FeCoNi)0.9Cr0.1 alloy changed both the magnitude and sign of the Cr-Cr CSRO parameter resulting in passivation behavior similar to 304L stainless steel containing twice the amount of Cr. Our analysis is based on comparing electrochemical measures of the kinetics of passive film formation with CSRO characterizations using time-of-flight neutron scattering, cluster expansion methods, density functional theory and Monte Carlo techniques. Our findings are interpreted within the framework of a recently proposed percolation theory of passivation that examines how selective dissolution of the non-passivating alloy components and CSRO results in excellent passive films at reduced levels of the passivating component.

cond-mat.mtrl-sci↗

arXiv2018

Pd$_{2}$Se$_{3}$ Monolayer: A Promising Two Dimensional Thermoelectric Material with Ultralow Lattice Thermal Conductivity and High Power Factor

A high power factor and low lattice thermal conductivity are two essential ingredients of highly efficient thermoelectric materials. Although monolayers of transition metal dichalcogenides possess high power factors, high lattice thermal conductivities significantly impede their practical applications. Our first-principles calculations show that these two ingredients are well fulfilled in the recently synthesized Pd$_{2}$Se$_{3}$ monolayer, whose crystal structure is composed of [Se$_{2}$]$^{2-}$ dimers, Se$^{2-}$ anions, and Pd$^{2+}$ cations coordinated in a square planar manner. Our detailed analysis of third-order interatomic force constants reveals that the anharmonicity and soft phonon modes associated with [Se$_2$]$^{2-}$ dimers lead to ultra-low lattice thermal conductivities in Pd$_{2}$Se$_{3}$ monolayers (1.5 and 2.9 Wm$^{-1}$K$^{-1}$ along the $a$- and $b$-axes at 300\,K respectively), which are comparable to those of high-performance bulk thermoelectric materials such as PbTe. Moreover, the "pudding-mold" type band structure, caused by Pd$^{2+}$ ($d^{8}$) cations coordinated in a square planar crystal field, leads to high power factors in Pd$_{2}$Se$_{3}$ monolayers. Consequently, both electron and hole doped thermoelectric materials with a considerably high $zT$ can be achieved at moderate carrier concentrations, suggesting that Pd$_{2}$Se$_{3}$ is a promising two-dimensional thermoelectric material.

cond-mat.mtrl-sci↗

arXiv2017

Computational Investigation of Inverse-Heusler compounds for Spintronics Applications

First-principles calculations of the electronic structure, magnetism and structural stability of inverse-Heusler compounds with the chemical formula \textit{X$_2$YZ} are presented and discussed with a goal of identifying compounds of interest for spintronics. Compounds for which the number of electrons per atom for \textit{Y} exceed that for \textit{X} and for which \textit{X} is one of Sc, Ti, V, Cr, Mn, Fe, Co, Ni, or Cu; \textit{Y} is one of Ti, V, Cr, Mn, Fe, Co, Ni, Cu, or Zn; and \textit{Z} is one of Al, Ga, In, Si, Ge, Sn, P, As or Sb were considered. The formation energy per atom of each compound was calculated. By comparing our calculated formation energies to those calculated for phases in the Inorganic Crystal Structure Database (ICSD) of observed phases, we estimate that inverse-Heuslers with formation energies within 0.052 eV/atom of the calculated convex hull are reasonably likely to be synthesizable in equilibrium. The observed trends in the formation energy and relative structural stability as the \textit{X}, \textit{Y} and \textit{Z} elements vary are described. In addition to the Slater-Pauling gap after 12 states per formula unit in one of the spin channels, inverse-Heusler phases often have gaps after 9 states or 14 states. We describe the origin and occurrence of these gaps. We identify 14 inverse-Heusler semiconductors, 51 half-metals and 50 near half-metals with negative formation energy. In addition, our calculations predict 4 half-metals and 6 near half-metals to lie close to the respective convex hull of stable phases, and thus may be experimentally realized under suitable synthesis conditions, resulting in potential candidates for future spintronics applications.

cond-mat.mtrl-sci↗

arXiv2016

Computational Investigation of Half-Heusler Compounds for Spintronics Applications

We present first-principles density functional calculations of the electronic structure, magnetism, and structural stability of 378 $\textit{XYZ}$ half-Heusler compounds (with $X=$ Cr, Mn, Fe, Co, Ni, Ru, Rh, $Y=$ Ti, V, Cr, Mn, Fe, Ni, $Z=$ Al, Ga, In, Si, Ge, Sn, P, As, Sb). We find that a "Slater-Pauling density of states" with a gap or pseudogap at three states per atom below the gap in at least one spin channel is a common feature in half-Heusler compounds. We find that the presence of such a gap at the Fermi energy in one or both spin channels contributes greatly to the stability of a half-Heusler compound. We calculate the formation energy of each compound and systematically investigate its stability against all other phases in the Open Quantum Materials Database (OQMD). We represent the thermodynamic phase stability of each compound as its distance from the convex hull of stable phases in the respective chemical space and show that the hull distance of a compound is a good measure of the likelihood of its experimental synthesis. We identify 26 18-electron semiconductors, 45 half-metals, and 34 near half-metals with negative formation energy, that follow the Slater-Pauling rule of three electrons per atom. Our calculations predict new thermodynamically stable semiconducting phases NiScAs, RhTiP, and RuVAs, which merit further experimental exploration. Further, two interesting zero-moment half-metals, CrMnAs and MnCrAs, are calculated to have negative formation energy. In addition, our calculations predict a number of new, hitherto unreported, semiconducting (e.g., CoVGe, FeVAs), half-metallic (e.g., RhVSb), near half-metallic (e.g., CoFeSb, CoVP) half-Heusler compounds to lie close to the respective convex hull of stable phases, and thus may be experimentally realized under suitable synthesis conditions, resulting in potential candidates for various spintronics applications.

cond-mat.mtrl-sci↗

arXiv2013

Thermodynamic Stability of Mg-based Ternary Long-Period Stacking Ordered Structures

Mg alloys containing long-period stacking ordered (LPSO) structures exhibit remarkably high tensile yield strength and ductility. They have been found in a variety of ternary Mg systems of the general form Mg-XL-XS, where XL and XS are elements larger and smaller than Mg, respectively. In this work, we examine the thermodynamic stability of these LPSO precipitates with density functional theory, using a newly proposed structure model based on the inclusion of a Mg interstitial atom. We predict the stabilities for 14H and 18R LPSO structures for many Mg-XL-XS ternary systems: 85 systems consisting of XL=rare earths (RE) Sc,Y,La-Lu and XS=Zn,Al,Cu,Co,Ni. We predict thermodynamically stable LPSO phases in all systems where LPSO structures are observed. In addition, we predict several stable LPSO structures in new, as-yet-unobserved Mg-RE-XS systems. Many non-RE XL elements are also explored on the basis of size mismatch between Mg and XL, including Tl,Sb,Pb,Na,Te,Bi,Pa,Ca,Th,K,Sr --- an additional 55 ternary systems. XL=Ca, Sr, and Th are predicted to be most promising to form stable LPSO phases, particularly with XS=Zn. Lastly, several previously observed trends amongst known XL elements are examined. We find that favorable mixing energy between Mg and XL on the FCC lattice and the size mismatch together serve as excellent criteria determining XL LPSO formation.

cond-mat.mtrl-sci↗

arXiv2008

First-Principles Theory of Competing Order Types, Phase Separation, and Phonon Scattering in Thermoelectric Pb-Sb-Ag-Te Alloys

Using a first-principles cluster expansion, we shed light on the solid-state phase diagram and structure of the recently discovered high-performance thermoelectrics, Pb-Ag-Sb-Te alloys. The observed nanoscale inhomogeneities are shown to be coherent precipitates of ordered (Ag)m(Sb)n(Te)m+n phases, such as AgSbTe2, all immiscible with rocksalt PbTe. The solubility is high for PbTe in AgSbTe2 and low for (Ag,Sb)Te in PbTe (8% vs. 0.6% at 850 K). The differences in the phonon spectra of PbTe and AgSbTe2 confirm that the inhomogeneities enhance the thermoelectric performance.

cond-mat.mtrl-sci↗

arXiv2007

Thermodynamic guidelines for the prediction of hydrogen storage reactions and their application to destabilized hydride mixtures

We propose a set of thermodynamic guidelines aimed at facilitating more robust screening of hydrogen storage reactions. The utility of the guidelines is illustrated by reassessing the validity of reactions recently proposed in the literature, and through vetting a list of more than 20 candidate reactions based on destabilized LiBH4 and Ca(BH4)2 borohydrides. Our analysis reveals several new reactions having both favorable thermodynamics and relatively high hydrogen densities (5-9 wt.% H2 & 85-100 g H2 /L), and demonstrates that chemical intuition alone is not sufficient to identify valid reaction pathways.

cond-mat.mtrl-sci↗

arXiv2007

Reaction energetics and crystal structure of Li4BN3H10 from first principles

Using density functional theory we examine the crystal structure and the finite-temperature thermodynamics of formation and dehydrogenation for the new quaternary hydride Li4BN3H10. Two recent studies based on X-ray and neutron diffraction have reported three bcc crystal structures for this phase. While these structures possess identical space groups and similar lattice constants, internal coordinate differences result in bond length discrepancies as large as 0.2 A. Geometry optimization calculations on the experimental structures reveal that the apparent discrepancies are an artifact of X-ray interactions with strong bond polarization; the relaxed structures are essentially identical. Regarding reaction energetics, the present calculations predict that the formation reaction 3LiNH2 + LiBH4 -> Li4BN3H10 is exothermic with enthalpy Delta H(T=300K) = -11.8 kJ/(mol f.u.), consistent with reports of spontaneous Li4BN3H10 formation in the literature. Calorimetry experiments have been reported for the dehydrogenation reaction, but have proven difficult to interpret. To help clarify the thermodynamics we evaluate the free energies of seventeen candidate dehydrogenation pathways over the temperature range T = 0-1000 K. At temperatures where H2 release has been experimentally observed (T \~ 520-630 K), the favored dehydrogenation reaction is Li4BN3H10 -> Li3BN2 + LiNH2 + 4 H2, which is weakly endothermic [Delta H(T=550K) = 12.8 kJ/(mol H2)]. The small calculated Delta H is consistent with the unsuccessful attempts at re-hydriding reported in the literature, and suggests that the moderately high temperatures needed for H-desorption result from slow kinetics.

cond-mat.mtrl-sci↗

arXiv1998

Cation- and vacancy-ordering in Li_xCoO_2

Using a combination of first-principles total energies, a cluster expansion technique, and Monte Carlo simulations, we have studied the Li/Co ordering in LiCoO_2 and Li-vacancy/Co ordering in CoO_2. We find: (i) A ground state search of the space of substitutional cation configurations yields the (layered) CuPt structure as the lowest-energy state in the octahedral system LiCoO_2 (and CoO_2), in agreement with the experimentally observed phase. (ii) Finite temperature calculations predict that the solid-state order- disorder transitions for LiCoO_2 and CoO_2 occur at temperatures (~5100 K and ~4400 K, respectively) much higher than melting, thus making these transitions experimentally inaccessible. (iii) The energy of the reaction E(LiCoO_2) - E(CoO_2) - E(Li) gives the average battery voltage V of a Li_xCoO_2/Li cell. Searching the space of configurations for large average voltages, we find that CuPt (a monolayer <111> superlattice) has a high voltage (V=3.78 V), but that this could be increased by cation randomization (V=3.99 V), partial disordering (V=3.86 V), or by forming a 2-layer Li_2Co_2O_4 superlattice along <111> (V=4.90 V).

cond-mat.mtrl-sci↗

arXiv1998

Evaluating and improving the cluster variation method entropy functional for Ising alloys

The success of the "Cluster Variation Method" (CVM) in reproducing quite accurately the free energies of Monte Carlo (MC) calculations on Ising models is explained in terms of identifying a cancellation of errors: We show that the CVM produces correlation functions that are too close to zero, which leads to an overestimation of the exact energy, E, and at the same time, to an underestimation of -TS, so the free energy F=E-TS is more accurate than either of its parts. This insight explains a problem with "hybrid methods" using MC correlation functions in the CVM entropy expression: They give exact energies E and do not give significantly improved -TS relative to CVM, so they do not benefit from the above noted cancellation of errors. Additionally, "hybrid methods" suffer from the difficulty of adequately accounting for both ordered and disordered phases in a consistent way. A different technique, the "Entropic Monte Carlo" (EMC), is shown here to provide a means for critically evaluating the CVM entropy. Inspired by EMC results, we find a universal and simple correction to the CVM entropy which produces individual components of the free energy with MC accuracy, but is computationally much less expensive than either MC thermodynamic integration or EMC.

cond-mat.mtrl-sci↗

arXiv1997

Effects of anharmonic strain on phase stability of epitaxial films and superlattices: applications to noble metals

Epitaxial strain energies of epitaxial films and bulk superlattices are studied via first-principles total energy calculations using the local-density approximation. Anharmonic effects due to large lattice mismatch, beyond the reach of the harmonic elasticity theory, are found to be very important in Cu/Au (lattice mismatch 12%), Cu/Ag (12%) and Ni/Au (15%). We find that <001> is the elastically soft direction for biaxial expansion of Cu and Ni, but it is <201> for large biaxial compression of Cu, Ag, and Au. The stability of superlattices is discussed in terms of the coherency strain and interfacial energies. We find that in phase-separating systems such as Cu-Ag the superlattice formation energies decrease with superlattice period, and the interfacial energy is positive. Superlattices are formed easiest on (001) and hardest on (111) substrates. For ordering systems, such as Cu-Au and Ag-Au, the formation energy of superlattices increases with period, and interfacial energies are negative. These superlattices are formed easiest on (001) or (110) and hardest on (111) substrates. For Ni-Au we find a hybrid behavior: superlattices along <111> and <001> like in phase-separating systems, while for <110> they behave like in ordering systems. Finally, recent experimental results on epitaxial stabilization of disordered Ni-Au and Cu-Ag alloys, immiscible in the bulk form, are explained in terms of destabilization of the phase separated state due to lattice mismatch between the substrate and constituents.

cond-mat.mtrl-sci↗

arXiv1997

Strain-induced shift in the elastically soft direction of epitaxially grown fcc metals

The theory of epitaxial strain energy is extended beyond the harmonic approximation to account for large film/substrate lattice mismatch. We find that for fcc noble metals (i) directions <001> and <111> soften under tensile biaxial strain (unlike zincblende semiconductors) while (ii) <110> and <201> soften under compressive biaxial strain. Consequently, (iii) upon sufficient compression <201> becomes the softest direction (lowest elastic energy), but (iv) <110> is the hardest direction for large tensile strain. (v) The dramatic softening of <001> in fcc noble metals upon biaxial tensile strain is caused by small fcc/bcc energy differences for these materials. These results can be used in selecting the substrate orientation for effective epitaxial growth of pure elements and A/sub p/B/sub q/ superlattices, as well as to explain the shapes of coherent precipitates in phase separating alloys.

cond-mat.mtrl-sci↗

arXiv1997

Cu-Au, Ag-Au, Cu-Ag and Ni-Au intermetallics: First-principles study of phase diagrams and structures

The classic metallurgical systems -- noble metal alloys -- that have formed the benchmark for various alloy theories, are revisited. First-principles fully relaxed general potential LAPW total energies of a few ordered structures are used as input to a mixed-space cluster expansion calculation to study the phase stability, thermodynamic properties and bond lengths in Cu-Au, Ag-Au, Cu-Ag and Ni-Au alloys. (i) Our theoretical calculations correctly reproduce the tendencies of Ag-Au and Cu-Au to form compounds and Ni-Au and Cu-Ag to phase separate at T=0 K. (ii) Of all possible structures, Cu/sub 3/Au (L1/sub 2/) and CuAu (L1/sub 0/) are found to be the most stable low-temperature phases of Cu/sub 1-x/Au/sub x/ with transition temperatures of 530 K and 660 K, respectively, compared to the experimental values 663 K and 670 K. The significant improvement over previous first-principles studies is attributed to the more accurate treatment of atomic relaxations in the present work. (iii) LAPW formation enthalpies demonstrate that L1/sub 2/, the commonly assumed stable phase of CuAu/sub 3/, is not the ground state for Au-rich alloys, but rather that ordered <100> superlattices are stabilized. (iv) We extract the non-configurational (e.g., vibrational) entropies of formation and obtain large values for the size mismatched systems: 0.48 k/sub B//atom in Ni/sub 0.5/Au/sub 0.5/ (T=1100 K), 0.37 k/sub B//atom in Cu/sub 0.14/Ag/sub 0.86/ (T=1052 K), and 0.16 k/sub B//atom in Cu/sub 0.5/Au/sub 0.5/ (T=800 K). (v) Using 8 atom/cell special quasirandom structures we study the bond lengths in disordered Cu-Au and Ni-Au alloys and obtain good qualitative agreement with recent EXAFS measurements.

cond-mat.mtrl-sci↗

arXiv1997

Ni-Au: A testing ground for theories of phase stability

The theory of phase stability in the Ni-Au alloy system is a popular topic due to the large size mismatch between Ni and Au, which makes the effects of atomic relaxation critical, and also the fact that Ni-Au exhibits a phase separation tendency at low temperatures, but measurements at high-temperature show an ordering-type short-range order. We have clarified the wide disparity which exists in the previously calculated values of mixing energies and thermodynamic properties by computing ``state-of-the-art'' energetics (full-potential, fully-relaxed LDA total energies) combined with ``state-of-the-art'' statistics (k-space cluster expansion with Monte Carlo simulations) for the Ni-Au system. We find: (i) LDA provides accurate mixing energies of disordered Ni_{1-x}Au_x alloys (ΔH_{mix} < +100 meV/atom) provided that both atomic relaxation (a ~100 meV/atom effect) and short-range order (~25 meV/atom) are taken into account properly. (ii) Previous studies using empirical potentials or approximated LDA methods often underestimate the formation energy of ordered compounds, and hence also underestimate the mixing energy of random alloys. (iii) Measured values of the total entropy of mixing combined with calculated values of the configurational entropy demonstrate that the non-configurational entropy in Ni-Au is large, and leads to a significant reduction in miscibillity gap temperature. (iv) The calculated short-range order agrees well with measurements, and both predict ordering in the disordered phase. (v) Consequently, using inverse Monte Carlo to extract interaction energies from the measured/calculated short-range order in Ni-Au would result in interactions which would produce ordering-type mixing energies, in contradiction with both experimental measurements and precise LDA energies.

cond-mat.mtrl-sci↗

arXiv1996

Invertible and Non-invertible Alloy Ising Models

Physical properties of alloys are compared as computed from ``direct'' and ``inverse'' procedures. The direct procedure involves Monte Carlo simulations of a set of local density approximation (LDA)-derived pair and multibody interactions {ν_f}, generating short-range order (SRO), ground states, order- disorder transition temperatures, and structural energy differences. The inverse procedure involves ``inverting'' the SRO generated from {ν_f} via inverse-Monte-Carlo to obtain a set of pair only interactions {\tildeν_f}. The physical properties generated from {\tildeν_f} are then compared with those from {ν_f}. We find that (i) inversion of the SRO is possible (even when {ν_f} contains multibody interactions but {\tildeν_f} does not) but, (ii) the resulting interactions {\tildeν_f} agree with the input interactions {ν_f} only when the problem is dominated by pair interactions. Otherwise, {\tildeν_f} are very different from {ν_f}. (iii) The same SRO pattern can be produced by drastically different sets {ν_f}. Thus, the effective interactions deduced from inverting SRO are not unique. (iv) Inverting SRO always misses configuration-independent (but composition- dependent) energies such as the volume deformation energy G(x); consequently, the ensuing {\tildeν_f} cannot be used to describe formation enthalpies or two-phase regions of the phase diagram, which depend on G(x).

cond-mat.mtrl-sci↗

arXiv1996

Point-charge electrostatics in disordered alloys

A simple analytic model of point-ion electrostatics has been previously proposed in which the magnitude of the net charge q_i on each atom in an ordered or random alloy depends linearly on the number N_i^(1) of unlike neighbors in its first coordination shell. Point charges extracted from recent large supercell (256-432 atom) local density approximation (LDA) calculations of Cu-Zn random alloys now enable an assessment of the physical validity and accuracy of the simple model. We find that this model accurately describes (i) the trends in q_i vs. N_i^(1), particularly for fcc alloys, (ii) the magnitudes of total electrostatic energies in random alloys, (iii) the relationships between constant-occupation-averaged charges and Coulomb shifts (i.e., the average over all sites occupied by either $A$ or $B$ atoms) in the random alloy, and (iv) the linear relation between the site charge q_i and the constant- charge-averaged Coulomb shift (i.e., the average over all sites with the same charge) for fcc alloys. However, for bcc alloys the fluctuations predicted by the model in the q_i vs. V_i relation exceed those found in the LDA supercell calculations. We find that (a) the fluctuations present in the model have a vanishing contribution to the electrostatic energy. (b) Generalizing the model to include a dependence of the charge on the atoms in the first three (two) shells in bcc (fcc) - rather than the first shell only - removes the fluctuations, in complete agreement with the LDA data. We also demonstrate an efficient way to extract charge transfer parameters of the generalized model from LDA calculations on small unit cells.

mtrl-th↗