Thermal Diffusivity in Metallic Nanowire Aerogels

Abstract

Metallic nanowire aerogels combine the functional properties of metals with the high porosity of aerogels. Here, Ag and Cu nanowire aerogels with densities of 20-500 mg cm-3 were synthesized by freeze casting and investigated using lock-in thermography during sequential mechanical compaction. Thermal transport depended strongly on nanowire diameter, with 30 nm Ag nanowires exhibiting substantially lower thermal diffusivity than 60 nm wires, likely due to enhanced surface scattering as the wire diameter approaches the electron mean free path in Ag. Surprisingly, increasing the aerogel density through mechanical compaction reduced the calculated thermal diffusivity by nearly 300x, opposite the conventional expectation that denser materials transport heat more efficiently. Further analysis showed that this decrease is dominated by the thickness term in the thermal diffusivity formalism, while the fitted transport coefficient changes comparatively little. The characteristic thermal diffusion timescale decreased only modestly during compaction, indicating that densification primarily collapses pore volume without fundamentally restructuring the conductive nanowire network. This behavior resembles topology-preserving densification, where large geometric compression produces comparatively small changes in the effective percolative transport pathway. These results show that nanowire aerogels cannot always be treated as homogeneous bulk media, because their macroscopic geometry and conductive network evolve differently during compaction.