Nd3+ Doping-induced Leakage Currents Suppression in High-temperature 0.7BiFeO3-0.3BaTiO3 Lead-free Piezoceramics

Abstract

BiFeO3 has attracted much attention as a potential candidate for replacing conventional, lead based piezoelectric materials due to its remarkable spontaneous polarization and high Curie temperature. However, its inherent high leakage currents, which lead to low piezoelectric response and poor temperature stability, have severely limited its practical applications. In this study, lead free piezoelectric ceramics of the 0.7BiFeO3-0.3BaTiO3 (BF-BT) system were prepared, and their microstructures along with high-temperature electrical performance were modulated by introducing Nd3+. The results indicate that moderate Nd doping improves lattice symmetry and reduces oxygen vacancy-related defect dipoles, thereby effectively suppressing leakage currents at temperatures above 75°C. The Nddoped samples exhibit significantly lower leakage current densities, reduced by over 99% compared to the undoped ceramics, reaching values as low as 10-5Acm-2. They also show higher resistivity under elevated temperatures and electric fields, offering notable improvements in thermal stability over the undoped counterparts. In addition, the Nd-doped samples achieved piezoelectric coefficients as high as 172 pC N -1 at room temperature while still maintaining high dielectric and piezoelectric responses at elevated temperatures. This work not only provides an effective way to solve the leakage current problem of BF-BT ceramics in high temperature applications but also indicates a new design strategy for optimizing the high temperature stability of lead free piezoelectric materials, which shows a broad application prospect in the field of high-temperature sensors and actuators.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Jinming Liu, Mingtong Chen, Zhengbao Yang. 2025-07-22. Nd3+ Doping-induced Leakage Currents Suppression in High-temperature 0.7BiFeO3-0.3BaTiO3 Lead-free Piezoceramics. https://arxiv.org/abs/2507.16156

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

Competing effects of Si and Mg doping on native point defects in yttrium aluminum garnet

We investigate how Si and Mg doping affect native point defects in yttrium aluminum garnet (YAG) by combining first-principles calculations with a thermodynamic model of defect equilibria. Formation energies and equilibrium concentrations of native defects, dopants, and defect complexes are obtained across the full range of oxygen chemical potentials relevant to ceramic sintering. Donor (Si) and acceptor (Mg) dopants are found to control native defect populations efficiently but in opposite directions: Si substantially raises cation-vacancy concentrations while suppressing oxygen vacancies, whereas Mg produces the reverse trend. Depending on dopant concentration and oxygen chemical potential, native vacancy concentrations vary by up to thirteen orders of magnitude. The concentration of isolated cation vacancies depends nonmonotonically on Si content, a consequence of Si-vacancy complex formation. Under Si-Mg co-doping, the two dopants compensate each other efficiently, giving rise to pronounced minima in both cation- and oxygen-vacancy concentrations when Si and Mg are present in equal amounts. These findings provide a microscopic basis for the pronounced sensitivity of YAG sintering behavior to the Si/Mg ratio, and show that balanced donor-acceptor co-doping is an effective strategy for controlling native defect populations in YAG.

cond-mat.mtrl-sci

Statistical admissibility and long-wavelength structural convergence determine representative support in granular materials

Representative elementary areas and volumes provide the scale bridge between resolved granular microstructure and continuum-scale material properties, yet they are still commonly selected from the apparent stabilization of a single scalar observable. Such plateaus can be false indicators of representativeness when statistically incompatible regions are averaged together or when long-wavelength structural correlations remain unresolved. We introduce a general representative-support framework for granular materials based on three sequential requirements: statistical admissibility of the sampled domain, persistent convergence of the apparent field mean and the low-wavenumber covariance spectrum, and validation against independent effective properties. The concept is tested on seven large-area backscattered-electron images of Arabian dune sands and mineral-resolved QEMSCAN maps. The structure-only criterion identifies a representative elementary area of $1536$ pixels, corresponding to approximately $2.01~\mathrm{mm}$. Without property-specific fitting or recalibration, the same physical scale transferred to the QEMSCAN grid $(\approx 2.04~\mathrm{mm})$ coincides with the onset of weak size dependence in apparent thermal conductivity, elastic stiffness, and directional Young's moduli. Thus, the representative scale inferred from long-wavelength granular organization independently predicts the convergence of distinct constitutive responses. The results show that representative support should be assigned only after both statistical compatibility and long-range structural convergence have been established. Although demonstrated here on two-dimensional dune-sand sections, the criterion is formulated for granular materials generally and has a direct mathematical extension to three-dimensional voxelized volumes.

cond-mat.mtrl-sci

Interplay of spin-lattice and electronic coupling far above Neel ordering in 2D antiferromagnetic CrPS4 and its interface manifestation

A short-range spin correlation driven, strongly intercoupled spin-phonon-electronic state far above TN (~38K) is identified in the low dimensional van der Waals antiferromagnet CrPS4. Temperature-dependent Raman spectroscopy reveals spin-phonon coupling persisting up to T*~120K, concomitant with local lattice distortion. The setting of vibronic progression in photoluminescence spectra suggests the strengthening of electron-phonon coupling around T*. Furthermore, both the electrical transport and optoelectronic response also change significantly at T*. The results indicate that spin-phonon coupling above TN in CrPS4 originates from local lattice distortion induced by short range magnetic correlations which in turn enhances the electron-phonon interaction. Furthermore, using a CrPS4/In2Se3 heterostructure, we demonstrate that the anomaly associated with the coupled degrees of freedom in CrPS4 also influences the adjacent In2Se3 layer. The lattice dynamics of In2Se3 is significantly modified across the magnetic anomaly of CrPS4, and the coupled dynamics is observed at T*. These interfacial manifestation opens up new possibilities for achieving correlated multifunctionalities in artificially designed heterostructure.

cond-mat.mtrl-sci