Crystallographic ordering of Al and Sn in {\alpha}-Ti
Abstract
Increasing attention is being paid to $\alpha$$_2$ Ti$_3$(Al,Sn) precipitation from the $\alpha$ phase of titanium alloys owing to its effect on slip band formation, localisation and the implications for fatigue performance in jet engine titanium. However, the early stages of $\alpha$$_2$ precipitation have historically been difficult to observe in TEM, neutron diffraction or atom probe analysis. Here, small angle X-ray scattering is used to reexamine the phase boundary in binary Ti-Al and Ti-Sn alloys with around 500 ppmw O. It is found that the phase boundaries in the literature are approximately correct, at 6.2 wt.% Al and 16.9 wt.% Sn, and that this favours the use of Al as a solid solution strengthener over Sn for ambient temperature applications. However, once O content and phase partitioning in $\alpha$+$\beta$ alloys are taken into account, this implies that Al$_{eq}$ limits for future alloy design of critical rotating parts should be lowered substantially.
Explore related subjects
Keep this discovery
Felicity F. Worsnop, Susannah L. M. Lea, Jan Ilavsky, David Rugg, David Dye. 2022-10-12. Crystallographic ordering of Al and Sn in {\alpha}-Ti. https://arxiv.org/abs/2210.06197
Cite the original work for its findings. Save a collection to share your selection of sources.