Evolution of Ge wetting layers growing on smooth and rough Si (001) surfaces: isolated {105} facets as a kinetic factor of stress relaxation

Larisa V. Arapkina·Kirill V. Chizh·Vladimir P. Dubkov·Mikhail S. Storozhevykh·Vladimir A. Yuryev
View original source ↗Read source document ↗Export metadata ↓

Abstract

The results of STM and RHEED studies of a thin Ge film grown on the Si/Si(001) epitaxial layers with different surface relief are presented. Process of the partial stress relaxation was accompanied by changes in the surface structure of the Ge wetting layer. Besides the well-known sequence of surface reconstructions ($2 \times 1 \rightarrow 2 \times N \rightarrow M \times N$ patches) and hut clusters faceted with {105} planes, the formation of isolated {105} planes, which faceted the edges of $M \times N$ patches, has been observed owing to the deposition of Ge on a rough Si/Si (001) surface. A model of the isolated {105} facet formation has been proposed based on the assumption that the mutual arrangement of the monoatomic steps on the initial Si surface promotes the wetting layer formation with the inhomogeneously distributed thickness that results in the appearance of $M \times N$ patches partially surrounded by deeper trenches than those observed in the usual Ge wetting layer grown on the smooth Si(001) surface. Isolated {105} facets are an inherent part of the Ge wetting layer structure and their formation decreases the surface energy of the Ge wetting layer.

Explore related subjects

cond-mat.mtrl-scicond-mat.mes-hall

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Larisa V. Arapkina, Kirill V. Chizh, Vladimir P. Dubkov, Mikhail S. Storozhevykh, Vladimir A. Yuryev. 2022-07-06. Evolution of Ge wetting layers growing on smooth and rough Si (001) surfaces: isolated {105} facets as a kinetic factor of stress relaxation. https://doi.org/10.1016/j.apsusc.2022.155094

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related papers

arXiv2026

Fine Oxide Dispersoids Modulate Phonon Drag and Dislocation Relaxation in Dynamically Deformed Superalloys

Plastic deformation in metallic alloys is primarily governed by the motion of dislocations, which are atomic scale line defects that move through the crystal lattice under an applied stress. Superalloys containing fine oxide particles withstand extreme temperatures for prolonged durations by resisting dislocation motion. This thermally controlled mechanism conventionally involves dislocations first climbing over the particle and slowly detaching from it, a process that typically occurs on the order of seconds. However, these mechanisms drastically change when dislocation velocities increase, potentially exceeding half the shear wave speed of the material. At such extreme speeds, dislocations can interact with lattice vibrations, leading to pronounced phonon interactions. We leverage a pulsed laser to drive rigid microspheres at controlled velocities towards superalloy substrates containing a dense oxide dispersion. Synchronized high speed imaging allows precise mapping of deformation events, allowing high throughput decoupling and modeling of plasticity contributions. We find that the oxide network produces a dual and counterintuitive effect. Our modeling framework indicates that rapidly moving dislocations bypass oxide particles by bowing rather than climbing, thereby suppressing departure side dislocation relaxation. At the same time, the dense oxide network confines fast moving dislocations within the critical interparticle distance, thereby reducing their interaction with phonons. These findings shed light on new plasticity mechanisms in oxide particle containing superalloys when line defects accelerate and dissipate energy on picosecond timescales.

cond-mat.mtrl-sci↗
arXiv2026

Oxygen deficiency and valency reconstruction in multiferroic V-doped HfO$_2$

The interplay of oxygen deficiency and vanadium multiple valency in the candidate multiferroic V-doped $Pca2_1$ hafnia HfO$_2$ is studied by first-principles calculations. Low-lying V majority gap states accept electrons from oxygen-vacancy donors, reducing their formation energy, and converting nominal V$^{4+}$ centers into V$^{3+}$. The resulting local magnetization and screening changes are reflected in the calculated V core-level shifts, which are consistent with the experimentally observed XPS signatures. The calculated V$^{3+}$/V$^{4+}$ population ratio determined by oxygen vacancies only matches experiment in reducing conditions, suggesting that additional electron reservoirs may contribute under ALD growth conditions. A similar scenario also seems to apply to the recently observed multiferroicity in Cr-doped hafnia, where oxygen deficiency is intrinsic to the growth technique.

cond-mat.mtrl-sci↗
arXiv2026

Defect-controlled twin activation in crystallographically equivalent magnesium micropillars

Tensile twinning plays a central role in accommodating -axis plasticity in Mg. In bulk Mg, it typically shows a relatively deterministic response with a low critical stress, whereas in confined volumes it exhibits broad yield-stress distributions that complicate the prediction of small-scale mechanical behavior. Here, site-specific compression tests are performed on 4 $μ$m-diameter pillars fabricated in a parent Mg crystal and an adjacent {10-12} twin. The two regions share the same [11-20] compression axis but experienced different prior deformation histories, allowing the influence of the residual microstructural state to be examined at fixed crystallographic orientation. Among 27 pillars, most parent-region pillars yield near 300 MPa, whereas pillars from the twin region span approximately 30 to 300 MPa. Interrupted tests combined with cross-sectional EBSD link individual load drops to discrete twin formation and further show that a pillar containing a pre-existing twin yields at approximately 80 MPa through the migration of the existing twin boundary. Molecular dynamics simulations of 30 nm-diameter pillars resolve possible atomistic pathways at the nanoscale. The simulations illustrate how contact geometry and pre-existing twin embryos alter event selection, and how an activated twin advances rapidly, while coherent twin boundary migration proceeds through disconnection motion accompanied by crystallographically required atomic shuffles. The results attribute the experimental scatter to the local availability of embryos and mobile interfaces, such that the first plastic event is governed by the twinning pathway accessible from the local microstructural state rather than by a single characteristic critical stress. Deformation history can therefore strongly modify the distribution of first plastic events even when the loading orientation is fixed.

cond-mat.mtrl-sci↗