Pulsed-laser epitaxy of metallic delafossite PdCrO$_2$ films

Abstract

Alternate stacking of a highly conducting metallic layer with a magnetic triangular layer found in delafossite PdCrO2 provides an excellent platform for discovering intriguing correlated quantum phenomena. Thin film growth of the material may enable not only tuning the basic physical properties beyond what bulk materials can exhibit, but also developing novel hybrid materials by interfacing with dissimilar materials, yet this has proven to be extremely challenging. Here, we report the epitaxial growth of metallic delafossite PdCrO2 films by pulsed laser epitaxy (PLE). The fundamental role of the PLE growth conditions, epitaxial strain, and chemical and structural characteristics of the substrate is investigated by growing under various growth conditions and on various types of substrates. While strain plays a large role in improving the crystallinities, the direct growth of epitaxial PdCrO2 films without impurity phases was not successful. We attribute this difficulty to both the chemical and structural dissimilarities between the substrates and volatile nature of PdO layer, which make nucleation of the right phase difficult. This difficulty was overcome by growing CuCrO2 buffer layers before PdCrO2 were grown. Unlike PdCrO2, CuCrO2 films were rather readily grown with a relatively wide growth window. Only monolayer thick buffer layer was sufficient to grow the correct PdCrO2 phase. This result indicates that the epitaxy of Pd-based delafossites is extremely sensitive to the chemistry and structure of the interface, necessitating near perfect substrate materials. The resulting films are commensurately strained and show an antiferromagnetic transition at 40 K that persists down to as thin as 3.6 nm in thickness.