Superconductivity in the Nb-Ru-Ge $σ$-Phase

Abstract

We show that the previously unreported ternary $σ$-phase material Nb$_{20.4}$Ru$_{5.7}$Ge$_{3.9}$ is a superconductor with a critical temperature of 2.2 K. Temperature-dependent magnetic susceptibility, resistance, and specific heat measurements were used to characterize the superconducting transition. The Sommerfeld constant $γ$ for Nb$_{20.4}$Ru$_{5.7}$Ge$_{3.9}$ is 91 mJ mol-f.u.$^{-1}$K$^{-2}$ and the specific heat anomaly at the superconducting transition, $Δ$C/$γ$T$_c$, is approximately 1.38. The zero-temperature upper critical field ($μ_0$H$_{c2}$(0)) was estimated to be 2 T by resistance data. Field-dependent magnetization data analysis estimated $μ_0$H$_{c1}$(0) to be 5.5 mT. Thus, the characterization shows Nb$_{20.4}$Ru$_{5.7}$Ge$_{3.9}$ to be a type II BCS superconductor. This material appears to be the first reported ternary phase in the Nb-Ru-Ge system, and the fact that there are no previously reported binary Nb-Ru, Nb-Ge, or Ru-Ge $σ$-phases shows that all three elements are necessary to stabilize the material. A $σ$-phase in the Ta-Ru-Ge system was synthesized but did not display superconductivity above 1.7 K, which suggests that electron count cannot govern the superconductivity observed. Preliminary characterization of a possible superconducting $σ$-phase in the Nb-Ru-Ga system is also reported.