Tuning the electronic hybridization in the heavy fermion cage compound YbFe$_{2}$Zn$_{20}$ with Cd-doping

Abstract

Tuning of the electronic properties of heavy fermion compounds by chemical substitutions provides excellent opportunities to further understand the physics of hybridized ions in crystal lattices. Here we present an investigation on the effects of Cd doping in flux-grown single crystals of the complex intermetallic cage compound YbFe$_{2}$Zn$_{20}$, that has been described as a heavy fermion with Sommerfeld coefficient of 535 mJ/mol.K$^{2}$. Substitution of Cd for Zn disturbs the system by expanding the unit cell and, in this case, the size of the Zn cages that surround Yb and Fe. With increasing amount of Cd, the hybridization between Yb $4f$ electrons and the conduction electrons is weakened, as evidenced by a decrease in the Sommerfeld coefficient, which should be accompanied by a valence shift of the Yb$^{3+}$ due to the negative chemical pressure effect. This scenario is also supported by the low temperature dc-magnetic susceptibility, that is gradually suppressed and evidences an increment of the Kondo temperature, based on a shift to higher temperatures of the characteristic broad susceptibility peak. Furthermore, the DC resistivity decreases with the isoelectronic Cd substitution for Zn, contrary to the expectation for an increasingly disordered system, and implying that the valence shift is not related to charge carrier doping. The combined results demonstrate excellent complementarity between positive physical pressure and negative chemical pressure, and point to a rich playground for exploring the physics and chemistry of strongly correlated electron systems in the general family of Zn$_{20}$ compounds, despite their structural complexity.